powder Coating

Product Introduction:

This product is formulated using phenolic epoxy resin and incorporates self-developed conductive polymers and conductive materials, combining the advantages of intrinsic and doped conductivity. It is specifically designed for conductive heavy-duty anti-corrosion powder coatings. The surface resistivity of the coating can reach below 10⁵ Ω, effectively eliminating static electricity accumulation in gas drainage pipes and preventing static sparks, thereby enhancing safety. The coating features high reactivity, strong adhesion, high cross-link density, and excellent resistance to chemicals, solvents, cathodic disbondment, as well as superior flexibility and impact resistance.

Product Features:

Excellent adhesion to the substrate.

Utilizes self-developed materials combining intrinsic and doped conductivity.

Good electrical conductivity of the coating, with surface resistivity reaching 10⁵ Ω, effectively eliminating surface charge accumulation.

Forms an anti-electric field at the coating-metal interface, shielding electron transfer and protecting the metal.

Superior high-temperature cathodic disbondment resistance.

Low melting temperature, high reactivity, high curing completion rate, and good mechanical properties.

Contains flame retardants, providing certain flame-retardant effects.

 

Powder Coating Performance Parameters

Item	Quality Indicator	Test Method
Appearance	Uniform color, no lumps	Visual inspection
Density (g/cm³)	1.3-1.7	GB/T 4472
Non-Volatile Content (%)	≥ 99.4	GB/T 6554

 

Cured Powder Coating Performance Parameters

Test Item	Technical Indicator	Test Method
Appearance	Smooth surface, uniform color, no bubbles, cracks, or pinholes	Visual inspection
Adhesion (Grade)	1-3	CJ/T 120-2008
Impact Resistance	No peeling, no cracking	CJ/T 120-2008
Surface Resistivity (Ω·m)	≤ 1×10⁶ (Ω·m)	GB/T 16906-97
Abrasion Resistance (1000g, 1000 cycles)	≤ 20g	GB/T 1768-1979
Alcohol Burner Flame Test	Average flaming combustion time ≤ 3s	MT 181-88
	Maximum flaming combustion time ≤ 10s
	Average non-flaming combustion time ≤ 20s
	Maximum non-flaming combustion time ≤ 60s
Bending Test	No stripping or cracking of the inner coating	CJ/T 120-2008
Flattening Test (Flattening ratio 4/5)	No cracking, no stripping	CJ/T 120-2008

 

Compliance Standard: MT 181-88

Application Fields:

Special anti-static and anti-corrosion coating for gas ventilation and drainage pipes in coal mines.

Application Processes:

Electrostatic spraying, dip coating, roll coating, etc.

Precautions:

The steel pipe surface should be free of oil and moisture; the surface treatment quality should reach Sa2 1/2 level (GB/T 8923); the anchor pattern depth should be 40-90 mm; dust and abrasives on the steel pipe surface should be blown clean. Preheating temperature should be controlled between 180-250°C and must not exceed 275°C.

The product should be stored in a well-ventilated, dry indoor environment with a temperature below 30°C, away from heat sources, corrosive chemicals, and chemical solvents, and protected from strong light exposure. The stacking height should not exceed four layers. Avoid long-term pressure and ensure the packaging box is sealed to prevent caking and moisture, which can affect fluidization performance.

To ensure thorough curing of the epoxy coating and better anti-corrosion performance, it is recommended to preheat the steel pipe surface to above 200°C to improve the curing completion rate.