Polyurethane waterproof coating A STD-939
We are a manufacturer based in China. We specialize in providing high-quality Polyurethane waterproof coating A STD-939 for industrial clients across various sectors. Whether you need chemicals consultation or technical support, our team is here to help.
Category：Coating raw materials Own Brand：MT /MOQ:100KG /From China/ B2B only.
Introduction
The polyurethane prepolymer has a high resin content with excellent ratio of NCO, which can form a highly dense and elastic waterproof membrane after being cured and shaped by the curing agent.Our company’s several types of polyurethane prepolymer, with our corresponding curing agent, can reach different levels of waterproof membrane.The mixture is easy to apply, and can be applied by roller application or spray application according to the requriement of the project.
After mixing the polyurethane prepolymer with its corresponding curing component in the recommended ratio and ensuring thorough stirring,apply it using roller coating or spray coating methods.
Product Features
Scientific configuration: High resin content with scientific ratio of NCO, ensuring excellent performance and durability.
High density and elasticity: The forming waterproof membrane that is highly dense and elastic, providing superior protection against water infiltration.
Easy application: The mixture of the polyurethane prepolymer and curing agent is supporting roller or spray application methods for convenient application on different surfaces.
Durable and reliable: The waterproof film formed by the polyurethane prepolymer is durable and reliable, providing long-lasting protection against water damage and leakage.
Parameter
| Item | 979-A | 939-A | 911C-A | 911D-A |
|---|---|---|---|---|
| NCO content (%, ±1) | 4.7 | 6.7 | 3.3 | 4.5 |
| Appearance | Colorless or pale yellow liquid | |||
| Viscosity (23 ± 2 °C, mPa. s) | 6000-10000 | 5000-8000 | 700-1200 | 4200-4800 |
| The physical properties of the membrane formed after mixing the polyurethane prepolymer with the MT compatible curing component. | ||||
| STD curing component | 979-B | 939-B | 911C-B | 911D-B |
| Weight ratio(A:B) | 1:01 | 1:02 | 1:03 | 1:04 |
| Solid content (%) | 98 | 98 | 92 | 92 |
| Tensile Strength (MPa) | 3.5 | 6 | 2 | 2 |
| Elongation at Break (%) | 450 | 450 | 500 | 500 |
| Tear Strength (N/mm) | 25 | 35 | 15 | 15 |
| Impermeability | 0.4MPa, 2h | 0.4MPa, 2h | 0.6MPa, 2h | 0.6MPa, 2h |
| Bonding Strength (MPa) | 2.5 | 2.5 | 1 | 1 |
Note: The physical property data mentioned above are solely based on tests conducted on samples of the membrane formed after mixing the polyurethane prepolymer with the STD compatible curing component and do not represent the physical properties of the polyurethane prepolymer itself.
If you're ready to take the next step, Leave your message below and we’ll reply soon. 20+ years of chemical manufacturing & export experience, a partner you can trust.
Inquiry
Factory & Shipment