Photovoltaics Industry-General type adhesive
We are a manufacturer based in China. We specialize in providing high-quality Photovoltaics Industry-General type adhesive for industrial clients across various sectors. Whether you need chemicals consultation or technical support, our team is here to help.
Category：Electronic Adhesive Own Brand：MT /MOQ:100KG /From China/ B2B only.
Introduction
| Test items | PA-3016（Adhesive） | PA-9001（Hardener） |
|---|---|---|
| Solid content（%） | 50±2 | 100% |
| Solvent | Ethyl acetate | None |
| 25℃，mpa.s（Viscosity） | 50-200 | 1750-3250 |
| Mixing ratio | 100 | 3.6 |
| Test items | PA-3018（Adhesive） | PA-9001（Hardener） |
|---|---|---|
| Solid content（%） | 50±2 | 100% |
| Solvent | Ethyl acetate | None |
| 25℃ mpa.s（Viscosity） | 50-200 | 1750-3250 |
| Mixing ratio | 100 | 4 |
-
Excellent performance when bonding with the second generation PVDF membrane material.
-
Fast curing speed.
-
High initial strength after curing.
-
Resistant to high temperature and humidity for a long time.
-
The fastness of EVA composite adhesive layer does not decrease after thermal encapsulation.
-
Excellent coating performance.
-
Good leveling performance.
-
Superior UV aging resistance.
-
No wrinkle defects after compound curing.
Application process
Coating method
Suitable for mainstream coating methods such as mesh rolls, blades, extrusion, etc.
Drying temperature
Suggested temperature: 80-100℃, according to drying situation.
Coating dry weight
8-10 g/m² is recommended.
Maturation conditions
For 50-60℃, suggested maturation time is 2-3 days. Can be adjusted and customized according to customer process.