Fluorine compound rubber

Product Introduction:

MT-FR1010MB is a newly developed high temperature flame retardant additive specially used for polycarbonate (PC). It does not contain bromine and chlorine compounds, has high solubility in polycarbonate, is used in small amounts, and does not need to be combined with other flame retardant synergists.

Application:

It is more advantageous in the field of producing fully transparent polycarbonate resins. The addition of FR1010MB has a very low impact on the transparency of the resin, and can basically maintain the original light transmittance of the resin, and has almost no effect on the physical properties of the basic resin itself.

Features:

MT-FR1010MB has good compatibility with the resin, and the addition amount is low, which will not affect the physical properties of the basic resin. In particular, it will not affect the heat resistance of the material. After adding the flame retardant, the glass transition temperature of the material basically does not change, and the performance will be relatively stable.

Performance	Test standard	PC raw material	Raw material + 1% FR1010MB
MFI(g/10min)	ASTM D-955	8.74	8.98
Tensile strength (MPa)	ASTM D-638	61.5	62.68
Elongation at break (%)	ASTM D-638	208.25	214.68
Flexural strength (MPa)	ASTM D-790	101.89	103.96
Flexural modulus (MPa)	ASTM D-790	2180.28	2285.76
Impact deflection (KJ/m2)	ASTM D-256	87.73	89.79
Flame retardancy	UL94 3.2mm	HB	V0
Glass transition temperature (℃)		151.19	152.63
Light transmittance (%)		86.39	85.99

If you're ready to take the next step, Leave your message below and we’ll reply soon. 20+ years of chemical manufacturing & export experience, a partner you can trust.