Automotive components powder coatings MT-A1230/MT-EN155G /MT-PE 55-9403
We are a manufacturer based in China. We specialize in providing high-quality Automotive components powder coatings MT-A1230/MT-EN155G /MT-PE 55-9403 for industrial clients across various sectors. Whether you need chemicals consultation or technical support, our team is here to help.
Category：powder Coating Own Brand：MT /MOQ:100KG /From China/ B2B only.
Introduction
Product Description
MT-A1230 series covers a wide range of powder coatings specifically designed to meet the extreme demands of automotive components. Demanding environments require high performance protection. MT-A1230 will enhance and protect automotive parts with excellent chemical, corrosion and chip resistance as well as the right aesthetic appearance exactly where it’s needed.
Powder properties
| Chemical Type | Epoxy-Polyester |
| Area of usage | Automotive mechatronic components and systems |
| Related Specifications | Brose 587000-110 / Group 2 |
| Appearance | Smooth |
| Gloss level (60°) | 52 ± 4 GU |
| Colour | Black |
| Recommended Film Thickness (µm) | 80 ± 40 µm |
| Density (g/cm3) | 1.46 ± 0.03 |
| Gel time (at 200 °C) | 36 – 54sec |
| Coverage at 60 µ
Coverage at 80 µ |
93.0 g/m2 or 10.8 m2/kg
124.0 g/m2 or 8.1 m2/kg |
| Application | Corona Only – Electrostatic (30 – 100 kV) |
| Storage | Under dry, cool (<25°C) conditions |
| Shelf life | At least 12 months from production date |
| Curing schedule
(at object temperature) |
10 minutes at 180°C
(please see curing window) |
Mechanical Tests
| Adhesion | DIN EN ISO 2409 | Gt 0 |
| Erichsen cupping | DIN EN ISO 1520 | ≥ 5 mm |
| Buchholz indentation | DIN EN ISO 2815 | > 80 |
| Cylindrical mandrel | DIN EN ISO 1519 | ≤ 6 mm |
Application
MT-A1230 powders can be applied by manual or automatic electrostatic spray equipment. It is recommended that for consistent application and appearance product be fluidized during application. Unused powder can be reclaimed using suitable equipment and recycled through the coating system.
Pre-treatment
Steel surfaces to be coated must be clean and free from grease. For maximum protection it is essential to pre-treat components prior to the application of MT-A1230. Iron Phosphate and Zinc Phosphate of ferrous metals improve corrosion resistance.
If you're ready to take the next step, Leave your message below and we’ll reply soon. 20+ years of chemical manufacturing & export experience, a partner you can trust.
Inquiry
Factory & Shipment